Hardness Conversion Tables
[ Home ]
HARDNESS CONVERSION TABLE (BASED ON BRINELL HARDNESS HB)
Brinell |
Brinell |
|
Rockwell Hardness |
Rockwell Superficial Hardness |
Approximate |
|||||
Indentation |
3000 kgf |
|
Rockwell A |
Rockwell B |
Rockwell C |
Rockwell D |
|
|
|
Tensile |
Diameter |
10 mm |
|
60 kgf |
100 kgf |
150 kgf |
100 kgf |
15 kgf |
30 kgf |
45 kgf |
Strength |
mm |
Ball |
Vickers |
Diamond |
1//16" ball |
Diamond |
Diamond |
1/16" ball |
1/16" ball |
1/16" ball |
ksi (MPa) |
|
HB |
HV |
HRA |
HRB |
HRC |
HRD |
HR15N |
HR30N |
HR45N |
|
--- |
--- |
940 |
85.6 |
--- |
68.0 |
76.9 |
93.2 |
84.4 |
75.4 |
--- |
--- |
--- |
920 |
85.3 |
--- |
67.5 |
76.5 |
93.0 |
84.0 |
74.8 |
--- |
--- |
--- |
900 |
85.0 |
--- |
67.0 |
76.1 |
92.9 |
83.6 |
74.2 |
--- |
--- |
767 |
880 |
84.7 |
--- |
66.4 |
75.7 |
92.7 |
83.1 |
73.6 |
--- |
--- |
757 |
860 |
84.4 |
--- |
65.9 |
75.3 |
92.5 |
82.7 |
73.1 |
--- |
|
|
|
|
|
|
|
|
|
|
|
2.25 |
745 |
840 |
84.1 |
--- |
65.3 |
74.8 |
92.3 |
82.2 |
72.2 |
--- |
--- |
733 |
820 |
83.8 |
--- |
64.7 |
74.3 |
92.1 |
81.7 |
71.8 |
--- |
--- |
722 |
800 |
83.4 |
--- |
64.0 |
73.8 |
91.8 |
81.1 |
71.0 |
--- |
2.30 |
712 |
--- |
--- |
--- |
--- |
--- |
--- |
--- |
--- |
--- |
--- |
710 |
780 |
83.0 |
--- |
63.3 |
73.3 |
91.5 |
80.4 |
70.2 |
--- |
--- |
698 |
760 |
82.6 |
--- |
62.5 |
72.6 |
91.2 |
79.7 |
69.4 |
--- |
|
|
|
|
|
|
|
|
|
|
|
--- |
684 |
740 |
82.2 |
--- |
61.8 |
72.1 |
91.0 |
79.1 |
68. |
--- |
2.35 |
682 |
737 |
82.2 |
--- |
61.7 |
72.0 |
91.0 |
79.0 |
68.5 |
--- |
--- |
670 |
720 |
81.8 |
--- |
61.0 |
71.5 |
90.7 |
78.4 |
67.7 |
--- |
--- |
656 |
700 |
81.3 |
--- |
60.1 |
70.8 |
90.3 |
77.6 |
66.7 |
--- |
2.40 |
653 |
697 |
81.2 |
--- |
60.0 |
70.7 |
90.2 |
77.5 |
66.5 |
--- |
|
|
|
|
|
|
|
|
|
|
|
--- |
647 |
690 |
81.1 |
--- |
59.7 |
70.5 |
90.1 |
77.2 |
66.2 |
--- |
--- |
638 |
680 |
80.8 |
--- |
59.2 |
70.1 |
89.8 |
76.8 |
65.7 |
--- |
--- |
630 |
670 |
80.6 |
--- |
58.8 |
69.8 |
89.7 |
76.4 |
65.3 |
--- |
2.45 |
627 |
667 |
80.5 |
--- |
58.7 |
69.7 |
89.6 |
76.3 |
65.1 |
--- |
|
|
|
|
|
|
|
|
|
|
|
2.50 |
--- 601 |
677 640 |
80.7 79.8 |
--- --- |
59.1 57.3 |
70.0 68.7 |
89.8 89.0 |
76.8 75.1 |
65.7 63.5 |
--- --- |
Brinell |
Brinell |
|
Rockwell Hardness |
Rockwell Superficial Hardness |
Approximate |
|||||
Indentation |
3000 kgf |
|
Rockwell A |
Rockwell B |
Rockwell C |
Rockwell D |
|
|
|
Tensile |
Diameter |
10 mm |
|
60 kgf |
100 kgf |
150 kgf |
100 kgf |
15 kgf |
30 kgf |
45 kgf |
Strength |
mm |
Ball |
Vickers |
Diamond |
1//16" ball |
Diamond |
Diamond |
1/16" ball |
1/16" ball |
1/16" ball |
ksi (MPa) |
|
HB |
HV |
HRA |
HRB |
HRC |
HRD |
HR15N |
HR30N |
HR45N |
|
|
|
|
|
|
|
|
|
|
|
|
2.55 |
--- 578 |
640 615 |
79.8 79.1 |
--- --- |
57.3 56.0 |
68.7 67.7 |
89.0 88.4 |
75.1 73.9 |
63.5 62.1 |
--- --- |
|
|
|
|
|
|
|
|
|
|
|
2.60 |
--- 555 |
607 591 |
78.8 78.4 |
--- --- |
55.6 54.7 |
67.4 66.7 |
88.1 87.8 |
73.5 72.7 |
61.6 60.6 |
--- 2055 |
|
|
|
|
|
|
|
|
|
|
|
2.65 |
--- 534 |
579 569 |
78.0 77.8 |
--- --- |
54.0 53.5 |
66.1 65.8 |
87.5 87.2 |
72.0 71.6 |
59.8 59.2 |
2015 1985 |
|
|
|
|
|
|
|
|
|
|
|
2.70 |
--- 514 |
553 547 |
77.1 76.9 |
--- --- |
52.5 52.1 |
65.0 64.7 |
86.7 86.5 |
70.7 70.3 |
58.0 57.6 |
1915 1890 |
|
|
|
|
|
|
|
|
|
|
|
2.75 |
--- --- 495 |
539 530 528 |
76.7 76.4 76.3 |
--- --- --- |
51.6 51.1 51.0 |
64.3 63.9 63.8 |
86.3 86.0 85.9 |
69.9 69.5 69.4 |
56.9 56.2 56.1 |
1855 1825 1820 |
|
|
|
|
|
|
|
|
|
|
|
2.80 |
--- 477 |
516 508 |
75.9 75.6 |
--- --- |
50.3 49.6 |
63.2 62.7 |
85.6 85.3 |
68.7 68.2 |
55.2 54.5 |
1780 1740 |
|
|
|
|
|
|
|
|
|
|
|
2.85 |
--- 461 |
495 491 |
75.1 74.9 |
--- --- |
48.8 48.5 |
61.9 61.7 |
84.9 84.7 |
67.4 67.2 |
53.5 53.2 |
1680 1670 |
|
|
|
|
|
|
|
|
|
|
|
2.90 |
--- 444 |
474 472 |
74.3 74.2 |
--- --- |
47.2 47.1 |
61.0 60.8 |
84.1 84.0 |
66.0 65.8 |
51.7 51.5 |
1595 1585 |
Brinell |
Brinell |
|
Rockwell Hardness |
Rockwell Superficial Hardness |
Approximate |
|||||
Indentation |
3000 kgf |
|
Rockwell A |
Rockwell B |
Rockwell C |
Rockwell D |
|
|
|
Tensile |
Diameter |
10 mm |
|
60 kgf |
100 kgf |
150 kgf |
100 kgf |
15 kgf |
30 kgf |
45 kgf |
Strength |
mm |
Ball |
Vickers |
Diamond |
1//16" ball |
Diamond |
Diamond |
1/16" ball |
1/16" ball |
1/16" ball |
ksi (MPa) |
|
HB |
HV |
HRA |
HRB |
HRC |
HRD |
HR15N |
HR30N |
HR45N |
|
|
|
|
|
|
|
|
|
|
|
|
2.95 |
429 |
455 |
73.4 |
--- |
45.7 |
59.7 |
83.4 |
64.6 |
49.9 |
1510 |
3.00 |
415 |
440 |
72.8 |
--- |
44.5 |
58.8 |
82.8 |
63.5 |
48.4 |
1460 |
3.05 |
401 |
425 |
72.0 |
--- |
43.1 |
57.8 |
82.0 |
62.3 |
46.9 |
1390 |
|
|
|
|
|
|
|
|
|
|
|
3.10 |
388 |
410 |
71.4 |
--- |
41.8 |
56.8 |
81.4 |
61.1 |
45.3 |
1330 |
3.15 |
375 |
396 |
70.6 |
--- |
40.4 |
55.7 |
80.6 |
59.9 |
43.6 |
1270 |
3.20 |
363 |
383 |
70.0 |
--- |
39.1 |
54.6 |
80.0 |
58.7 |
42.0 |
1220 |
3.25 |
352 |
372 |
69.3 |
(110.0) |
37.9 |
53.8 |
79.3 |
57.6 |
40.5 |
1180 |
3.30 |
341 |
360 |
68.7 |
(109.0) |
36.6 |
52.8 |
78.6 |
56.4 |
39.1 |
1130 |
|
|
|
|
|
|
|
|
|
|
|
3.35 |
331 |
350 |
68.1 |
(108.5) |
35.5 |
51.9 |
78.0 |
55.4 |
37.8 |
1095 |
3.40 |
321 |
339 |
67.5 |
(108.0) |
34.3 |
51.0 |
77.3 |
54.3 |
36.4 |
1060 |
3.45 |
311 |
328 |
66.9 |
(107.5) |
33.1 |
50.0 |
76.7 |
53.3 |
34.4 |
1025 |
3.50 |
302 |
319 |
66.3 |
(107.0) |
32.1 |
49.3 |
76.1 |
52.2 |
33.8 |
1005 |
3.55 |
293 |
309 |
65.7 |
(106.0) |
30.9 |
48.3 |
75.5 |
51.2 |
32.4 |
970 |
|
|
|
|
|
|
|
|
|
|
|
3.60 |
285 |
301 |
65.3 |
(105.5) |
29.9 |
47.6 |
75.0 |
50.3 |
31.2 |
950 |
3.65 |
277 |
292 |
64.6 |
(104.5) |
28.8 |
46.7 |
74.4 |
49.3 |
29.9 |
925 |
3.70 |
269 |
284 |
64.1 |
(104.0) |
27.6 |
45.9 |
73.7 |
48.3 |
28.5 |
895 |
3.75 |
262 |
276 |
63.6 |
(103.0) |
26.6 |
45.0 |
73.1 |
47.3 |
27.3 |
875 |
3.80 |
255 |
269 |
63.0 |
(102.0) |
25.4 |
44.2 |
72.5 |
46.2 |
26.0 |
850 |
Brinell |
Brinell |
|
Rockwell Hardness |
Rockwell Superficial Hardness |
Approximate |
|||||
Indentation |
3000 kgf |
|
Rockwell A |
Rockwell B |
Rockwell C |
Rockwell D |
|
|
|
Tensile |
Diameter |
10 mm |
|
60 kgf |
100 kgf |
150 kgf |
100 kgf |
15 kgf |
30 kgf |
45 kgf |
Strength |
mm |
Ball |
Vickers |
Diamond |
1//16" ball |
Diamond |
Diamond |
1/16" ball |
1/16" ball |
1/16" ball |
ksi (MPa) |
|
HB |
HV |
HRA |
HRB |
HRC |
HRD |
HR15N |
HR30N |
HR45N |
|
3.85 |
248 |
261 |
62.5 |
(101.0) |
24.2 |
43.2 |
71.7 |
45.1 |
24.5 |
825 |
3.90 |
241 |
253 |
61.8 |
100.0 |
22.8 |
42.0 |
70.9 |
43.9 |
22.8 |
800 |
3.95 |
235 |
247 |
61.4 |
99.0 |
21.7 |
41.4 |
70.3 |
42.9 |
21.5 |
785 |
4.00 |
229 |
241 |
60.8 |
98.2 |
20.5 |
40.5 |
69.7 |
41.9 |
20.1 |
765 |
4.05 |
223 |
234 |
|
97.3 |
(18.8) |
--- |
--- |
--- |
--- |
--- |
|
|
|
|
|
|
|
|
|
|
|
4.10 |
217 |
228 |
--- |
96.4 |
(17.5) |
--- |
--- |
--- |
--- |
725 |
4.15 |
212 |
222 |
--- |
95.5 |
(16.0) |
--- |
--- |
--- |
--- |
705 |
4.20 |
207 |
218 |
--- |
94.6 |
(15.2) |
--- |
--- |
--- |
--- |
690 |
4.25 |
201 |
212 |
--- |
93.8 |
(13.8) |
--- |
--- |
--- |
--- |
675 |
4.30 |
197 |
207 |
--- |
92.8 |
(12.7) |
--- |
--- |
--- |
--- |
655 |
|
|
|
|
|
|
|
|
|
|
|
4.35 |
192 |
202 |
--- |
91.9 |
(11.5) |
--- |
--- |
--- |
--- |
640 |
4.40 |
187 |
196 |
--- |
90.7 |
(10.0) |
--- |
--- |
--- |
--- |
620 |
4.45 |
183 |
192 |
--- |
90.0 |
(9.0) |
--- |
--- |
--- |
--- |
615 |
4.50 |
179 |
188 |
--- |
89.0 |
(8.0) |
--- |
--- |
--- |
--- |
600 |
4.55 |
174 |
182 |
--- |
87.8 |
(6.4) |
--- |
--- |
--- |
--- |
585 |
|
|
|
|
|
|
|
|
|
|
|
4.60 |
170 |
178 |
--- |
86.8 |
(5.4) |
--- |
--- |
--- |
--- |
570 |
4.65 |
167 |
175 |
--- |
86.0 |
(4.4) |
--- |
--- |
--- |
--- |
560 |
4.70 |
163 |
171 |
--- |
85.0 |
(3.3) |
--- |
--- |
--- |
--- |
545 |
4.80 |
156 |
163 |
--- |
82.9 |
(0.9) |
--- |
--- |
--- |
--- |
525 |
4.90 |
149 |
156 |
--- |
80.8 |
--- |
--- |
--- |
--- |
--- |
505 |
Brinell |
Brinell |
|
Rockwell Hardness |
Rockwell Superficial Hardness |
Approximate |
|||||
Indentation |
3000 kgf |
|
Rockwell A |
Rockwell B |
Rockwell C |
Rockwell D |
|
|
|
Tensile |
Diameter |
10 mm |
|
60 kgf |
100 kgf |
150 kgf |
100 kgf |
15 kgf |
30 kgf |
45 kgf |
Strength |
mm |
Ball |
Vickers |
Diamond |
1//16" ball |
Diamond |
Diamond |
1/16" ball |
1/16" ball |
1/16" ball |
ksi (MPa) |
|
HB |
HV |
HRA |
HRB |
HRC |
HRD |
HR15N |
HR30N |
HR45N |
|
5.00 |
143 |
150 |
--- |
78.7 |
--- |
--- |
--- |
--- |
--- |
490 |
5.10 |
137 |
143 |
--- |
76.4 |
--- |
--- |
--- |
--- |
--- |
460 |
5.20 |
131 |
137 |
--- |
74.0 |
--- |
--- |
--- |
--- |
--- |
450 |
5.30 |
126 |
132 |
--- |
72.0 |
--- |
--- |
--- |
--- |
--- |
435 |
5.40 |
121 |
127 |
--- |
69.8 |
--- |
--- |
--- |
--- |
--- |
415 |
|
|
|
|
|
|
|
|
|
|
|
5.50 |
116 |
122 |
--- |
67.6 |
--- |
--- |
--- |
--- |
--- |
400 |
5.60 |
111 |
117 |
--- |
65.7 |
--- |
--- |
--- |
--- |
--- |
385 |
|
|
|
|
|
|
|
|
|
|
|
HARDNESS CONVERSION TABLE (BASED ON HRC)
|
|
Brinell |
Rockwell Hardness |
Rockwell Superficial Hardness |
|
|
||||
Rockwell C |
|
3000 kgf |
Rockwell A |
Rockwell B |
Rockwell D |
|
|
|
Approximate |
Rockwell C |
150 kgf |
Vickers |
10 mm |
60 kgf |
100 kgf |
100 kgf |
15 kgf |
30 kgf |
45 kgf |
Tensile |
150 kgf |
Diamond |
Hardness |
Ball |
Diamond |
1//16" ball |
Diamond |
1/16" ball |
1/16" ball |
1/16" ball |
Strength |
Diamond |
HRC |
HV |
HB |
HRA |
HRB |
HRD |
HR15N |
HR30N |
HR45N |
ksi (MPa) |
HRC |
68 |
940 |
--- |
85.6 |
--- |
76.9 |
93.2 |
84.4 |
75.4 |
--- |
68 |
67 |
900 |
--- |
85.0 |
--- |
76.1 |
92.9 |
83.6 |
74.2 |
--- |
67 |
66 |
865 |
--- |
84.5 |
--- |
75.4 |
92.5 |
82.8 |
73.3 |
--- |
66 |
65 |
832 |
739 |
83.9 |
--- |
74.5 |
92.2 |
81.9 |
72.0 |
--- |
65 |
64 |
800 |
722 |
83.4 |
--- |
73.8 |
91.8 |
81.1 |
71.0 |
--- |
64 |
|
|
|
|
|
|
|
|
|
|
|
63 |
772 |
705 |
82.8 |
--- |
73.0 |
91.4 |
80.1 |
69.9 |
--- |
63 |
62 |
746 |
688 |
82.3 |
--- |
72.2 |
91.1 |
79.3 |
68.8 |
--- |
62 |
61 |
720 |
670 |
81.8 |
--- |
71.5 |
90.7 |
78.4 |
67.7 |
--- |
61 |
60 |
697 |
654 |
81.2 |
--- |
70.7 |
90.2 |
77.5 |
66.6 |
--- |
60 |
59 |
674 |
634 |
80.7 |
--- |
69.9 |
89.8 |
76.6 |
65.5 |
--- |
59 |
|
|
|
|
|
|
|
|
|
|
|
58 |
653 |
615 |
80.1 |
--- |
69.2 |
89.3 |
75.7 |
64.3 |
--- |
58 |
57 |
633 |
595 |
79.6 |
--- |
68.5 |
88.9 |
74.8 |
63.2 |
--- |
57 |
56 |
613 |
577 |
79.0 |
--- |
67.7 |
88.3 |
73.9 |
62.0 |
--- |
56 |
55 |
595 |
560 |
78.5 |
--- |
66.9 |
87.9 |
73.0 |
60.9 |
2075 |
55 |
54 |
577 |
543 |
78.0 |
--- |
66.1 |
87.4 |
72.0 |
59.8 |
2015 |
54 |
|
|
|
|
|
|
|
|
|
|
|
53 |
560 |
525 |
77.4 |
--- |
65.4 |
86.9 |
71.2 |
58.6 |
1950 |
53 |
52 |
544 |
512 |
76.8 |
--- |
64.6 |
86.4 |
70.2 |
57.4 |
1880 |
52 |
51 |
528 |
496 |
76.3 |
--- |
63.8 |
85.9 |
69.4 |
56.1 |
1820 |
51 |
50 |
513 |
481 |
75.9 |
--- |
63.1 |
85.5 |
68.5 |
55.0 |
1760 |
50 |
49 |
498 |
469 |
75.2 |
--- |
62.1 |
85.0 |
67.6 |
53.8 |
1695 |
49 |
|
|
Brinell |
Rockwell Hardness |
Rockwell Superficial Hardness |
|
|
||||
Rockwell C |
|
3000 kgf |
Rockwell A |
Rockwell B |
Rockwell D |
|
|
|
Approximate |
Rockwell C |
150 kgf |
Vickers |
10 mm |
60 kgf |
100 kgf |
100 kgf |
15 kgf |
30 kgf |
45 kgf |
Tensile |
150 kgf |
Diamond |
Hardness |
Ball |
Diamond |
1//16" ball |
Diamond |
1/16" ball |
1/16" ball |
1/16" ball |
Strength |
Diamond |
HRC |
HV |
HB |
HRA |
HRB |
HRD |
HR15N |
HR30N |
HR45N |
ksi (MPa) |
HRC |
48 |
484 |
455 |
74.7 |
--- |
61.4 |
84.5 |
66.7 |
52.5 |
1635 |
48 |
47 |
471 |
443 |
74.1 |
--- |
60.8 |
83.9 |
65.8 |
51.4 |
1580 |
47 |
46 |
458 |
432 |
73.6 |
--- |
60.0 |
83.5 |
64.8 |
50.3 |
1530 |
46 |
45 |
446 |
421 |
73.1 |
--- |
59.2 |
83.0 |
64.0 |
49.0 |
1480 |
45 |
44 |
434 |
409 |
72.5 |
--- |
58.5 |
82.5 |
63.1 |
47.8 |
1435 |
44 |
|
|
|
|
|
|
|
|
|
|
|
43 |
423 |
400 |
72.0 |
--- |
57.7 |
82.0 |
62.2 |
46.7 |
1385 |
43 |
42 |
412 |
390 |
71.5 |
--- |
56.9 |
81.5 |
61.3 |
45.5 |
1340 |
42 |
41 |
402 |
381 |
70.9 |
--- |
56.2 |
80.9 |
60.4 |
44.3 |
1295 |
41 |
40 |
392 |
371 |
70.4 |
--- |
55.4 |
80.4 |
59.5 |
43.1 |
1250 |
40 |
39 |
382 |
362 |
69.9 |
--- |
54.6 |
79.9 |
58.6 |
41.9 |
1215 |
39 |
|
|
|
|
|
|
|
|
|
|
|
38 |
372 |
353 |
69.4 |
--- |
53.8 |
79.4 |
57.7 |
40.8 |
1180 |
38 |
37 |
363 |
344 |
68.9 |
--- |
53.1 |
78.8 |
56.8 |
39.6 |
1160 |
37 |
36 |
354 |
336 |
68.4 |
(109.0) |
52.3 |
78.3 |
55.9 |
38.4 |
1115 |
36 |
35 |
345 |
327 |
67.9 |
(108.5) |
51,5 |
77.7 |
55.0 |
37.2 |
1080 |
35 |
34 |
336 |
319 |
67.4 |
(108.0) |
50.8 |
77.2 |
54.2 |
36.1 |
1055 |
34 |
|
|
|
|
|
|
|
|
|
|
|
33 |
327 |
311 |
66.8 |
(107.5) |
50.0 |
76.6 |
53.3 |
34.9 |
1025 |
33 |
32 |
318 |
301 |
66.3 |
(107.0) |
49.2 |
76.1 |
52.1 |
33.7 |
1000 |
32 |
31 |
310 |
294 |
65.8 |
(106.0) |
48.4 |
75.6 |
51.3 |
32.5 |
980 |
31 |
30 |
302 |
286 |
65.3 |
(105.5) |
47.7 |
75.0 |
50.4 |
31.3 |
950 |
30 |
29 |
294 |
279 |
64.7 |
(104.5) |
47.0 |
74.5 |
49.5 |
30.1 |
930 |
29 |
|
|
Brinell |
Rockwell Hardness |
Rockwell Superficial Hardness |
|
|
||||
Rockwell C |
286 |
3000 kgf |
Rockwell A |
Rockwell B |
Rockwell D |
|
|
|
Approximate |
Rockwell C |
150 kgf |
Vicke279rs |
10 mm |
60 kgf |
100 kgf |
100 kgf |
15 kgf |
30 kgf |
45 kgf |
Tensile |
150 kgf |
Diamond |
Hardnes272s |
Ball |
Diamond |
1//16" ball |
Diamond |
1/16" ball |
1/16" ball |
1/16" ball |
Strength |
Diamond |
HRC |
HV |
HB |
HRA |
HRB |
HRD |
HR15N |
HR30N |
HR45N |
ksi (MPa) |
HRC |
28 |
286 |
271 |
64.3 |
(104.0) |
46.1 |
73.9 |
48.6 |
28.9 |
910 |
28 |
27 |
279 |
264 |
63.8 |
(103.0) |
45.2 |
73.3 |
47.7 |
27.8 |
880 |
27 |
26 |
272 |
258 |
63.3 |
(102.5) |
44.6 |
72.8 |
46.8 |
26.7 |
860 |
26 |
25 |
266 |
253 |
62.8 |
(101.5) |
43.8 |
72.2 |
45.9 |
25.5 |
840 |
25 |
24 |
260 |
247 |
62.4 |
(101.0) |
43.1 |
71.6 |
45.0 |
24.3 |
825 |
24 |
|
|
|
|
|
|
|
|
|
|
|
23 |
254 |
243 |
62.0 |
100.0 |
42.1 |
71.0 |
44.0 |
23.1 |
805 |
23 |
22 |
248 |
237 |
61.5 |
99.0 |
41.6 |
70.5 |
43.2 |
22.0 |
785 |
22 |
21 |
243 |
231 |
61.0 |
98.5 |
40.9 |
69.9 |
42.3 |
20.7 |
770 |
21 |
20 |
238 |
226 |
60.5 |
97.8 |
40.1 |
69.4 |
41.5 |
19.6 |
760 |
20 |
(18) |
230 |
219 |
--- |
96.7 |
--- |
--- |
--- |
--- |
730 |
(18) |
|
|
|
|
|
|
|
|
|
|
|
(16) |
222 |
212 |
--- |
95.5 |
--- |
--- |
--- |
--- |
705 |
(16) |
(14) |
213 |
203 |
--- |
93.9 |
--- |
--- |
--- |
--- |
675 |
(14) |
(12) |
204 |
194 |
--- |
92.3 |
--- |
--- |
--- |
--- |
650 |
(12) |
(10) |
196 |
187 |
--- |
90.7 |
--- |
--- |
--- |
--- |
620 |
(10) |
(8) |
188 |
179 |
--- |
89.5 |
--- |
--- |
--- |
--- |
600 |
(8) |
|
|
|
|
|
|
|
|
--- |
|
|
(6) |
180 |
171 |
--- |
87.1 |
--- |
--- |
--- |
--- |
580 |
(6) |
(4) |
173 |
165 |
--- |
85.5 |
--- |
--- |
--- |
--- |
550 |
(4) |
(2) |
166 |
158 |
--- |
83.5 |
--- |
--- |
--- |
--- |
530 |
(2) |
(0) |
160 |
152 |
--- |
81.7 |
--- |
--- |
--- |
--- |
510 |
(0) |
Rockwell C |
Vickers |
Brinell Hardness |
Knoop |
Rockwell Hardness Number |
Rockwell Superficial |
Scleroscope |
Rockwell C |
||||
10-mm Standard Ball, 3000-kgf (HBS) |
10-mm Carbide Ball, 3000-kgf (HBW) |
A Scale, 60-kgf (HRA) |
D Scale, 100-kgf (HRD) |
15-N Scale, 15-kgf (HR 15-N) |
30-N Scale, 30-kgf (HR 30-N) |
45-N Scale, 45-kgf (HR 45-N) |
|||||
68 | 940 | --- | --- | 920 | 85.6 | 76.9 | 93.2 | 84.4 | 75.4 | 97.3 | 68 |
67 | 900 | --- | --- | 895 | 85.0 | 76.1 | 92.9 | 83.6 | 74.2 | 95.0 | 67 |
66 | 865 | --- | --- | 870 | 84.5 | 75.4 | 92.5 | 82.8 | 73.3 | 92.7 | 66 |
65 | 832 | --- | (739) | 846 | 83.9 | 74.5 | 92.2 | 81.9 | 72.0 | 90.6 | 65 |
64 | 800 | --- | (722) | 822 | 83.4 | 73.8 | 91.8 | 81.1 | 71.0 | 88.5 | 64 |
63 | 772 | --- | (705) | 799 | 82.8 | 73.0 | 91.4 | 80.1 | 69.9 | 86.5 | 63 |
62 | 746 | --- | (688) | 776 | 82.3 | 72.2 | 91.1 | 79.3 | 68.8 | 84.5 | 62 |
61 | 720 | --- | (670) | 754 | 81.8 | 71.5 | 90.7 | 78.4 | 67.7 | 82.6 | 61 |
60 | 697 | --- | (654) | 732 | 81.2 | 70.7 | 90.2 | 77.5 | 66.6 | 80.8 | 60 |
59 | 674 | --- | 634 | 710 | 80.7 | 69.9 | 89.8 | 76.6 | 65.5 | 79.0 | 59 |
58 | 653 | --- | 615 | 690 | 80.1 | 69.2 | 89.3 | 75.7 | 64.3 | 77.3 | 58 |
57 | 633 | --- | 595 | 670 | 79.6 | 68.5 | 88.9 | 74.8 | 63.2 | 75.6 | 57 |
56 | 613 | --- | 577 | 650 | 79.0 | 67.7 | 88.3 | 73.9 | 62.0 | 74.0 | 56 |
55 | 595 | --- | 560 | 630 | 78.5 | 66.9 | 87.9 | 73.0 | 60.9 | 72.4 | 55 |
54 | 577 | --- | 543 | 612 | 78.0 | 66.1 | 87.4 | 72.0 | 59.8 | 70.9 | 54 |
53 | 560 | --- | 525 | 594 | 77.4 | 65.4 | 86.9 | 71.2 | 58.6 | 69.4 | 53 |
52 | 544 | (500) | 512 | 576 | 76.8 | 64.6 | 86.4 | 70.2 | 57.4 | 67.9 | 52 |
51 | 528 | (487) | 496 | 558 | 76.3 | 63.8 | 85.9 | 69.4 | 56.1 | 66.5 | 51 |
50 | 513 | (475) | 481 | 542 | 75.9 | 63.1 | 85.5 | 68.5 | 55.0 | 65.1 | 50 |
49 | 498 | (464) | 469 | 526 | 75.2 | 62.1 | 85.0 | 67.6 | 53.8 | 63.7 | 49 |
48 | 484 | 451 | 455 | 510 | 74.7 | 61.4 | 84.5 | 66.7 | 52.5 | 62.4 | 48 |
47 | 471 | 442 | 443 | 495 | 74.1 | 60.8 | 83.9 | 65.8 | 51.4 | 61.1 | 47 |
46 | 458 | 432 | 432 | 480 | 73.6 | 60.0 | 83.5 | 64.8 | 50.3 | 59.8 | 46 |
Rockwell C Hardness Number 150 kgf (HRC) |
Vickers Hardness Number (HV) |
Brinell Hardness Number C |
Knoop Hardness, Number 500-gf and Over (HK) |
Rockwell Hardness Number |
Rockwell Superficial Hardness Number |
Scleroscope Hardness Number D |
Rockwell C Hardness Number 150 kgf (HRC) |
||||
10-mm Standard Ball, 3000-kgf (HBS) |
10-mm Carbide Ball, 3000-kgf (HBW) |
A Scale, 60-kgf (HRA) |
D Scale, 100-kgf (HRD) |
15-N Scale, 15-kgf (HR 15-N) |
30-N Scale, 30-kgf (HR 30-N) |
45-N Scale, 45-kgf (HR 45-N) |
|||||
45 | 446 | 421 | 421 | 466 | 73.1 | 59.2 | 83.0 | 64.0 | 49.0 | 58.5 | 45 |
44 | 434 | 409 | 409 | 452 | 72.5 | 58.5 | 82.5 | 63.1 | 47.8 | 57.3 | 44 |
43 | 423 | 400 | 400 | 438 | 72.0 | 57.7 | 82.0 | 62.2 | 46.7 | 56.1 | 43 |
42 | 412 | 390 | 390 | 426 | 71.5 | 56.9 | 81.5 | 61.3 | 45.5 | 54.9 | 42 |
41 | 402 | 381 | 381 | 414 | 70.9 | 56.2 | 80.9 | 60.4 | 44.3 | 53.7 | 41 |
40 | 392 | 371 | 371 | 402 | 70.4 | 55.4 | 80.4 | 59.5 | 43.1 | 52.6 | 40 |
39 | 382 | 362 | 362 | 391 | 69.9 | 54.6 | 79.9 | 58.6 | 41.9 | 51.5 | 39 |
38 | 372 | 353 | 353 | 380 | 69.4 | 53.8 | 79.4 | 57.7 | 40.8 | 50.4 | 38 |
37 | 363 | 344 | 344 | 370 | 68.9 | 53.1 | 78.8 | 56.8 | 39.6 | 49.3 | 37 |
36 | 354 | 336 | 336 | 360 | 68.4 | 52.3 | 78.3 | 55.9 | 38.4 | 48.2 | 36 |
35 | 345 | 327 | 327 | 351 | 67.9 | 51.5 | 77.7 | 55.0 | 37.2 | 47.1 | 35 |
34 | 336 | 319 | 319 | 342 | 67.4 | 50.8 | 77.2 | 54.2 | 36.1 | 46.1 | 34 |
33 | 327 | 311 | 311 | 334 | 66.8 | 50.0 | 76.6 | 53.3 | 34.9 | 45.1 | 33 |
32 | 318 | 301 | 301 | 326 | 66.3 | 49.2 | 76.1 | 52.1 | 33.7 | 44.1 | 32 |
31 | 310 | 294 | 294 | 318 | 65.8 | 48.4 | 75.6 | 51.3 | 32.5 | 43.1 | 31 |
30 | 302 | 286 | 286 | 311 | 65.3 | 47.7 | 75.0 | 50.4 | 31.3 | 42.2 | 30 |
29 | 294 | 279 | 279 | 304 | 64.8 | 47.0 | 74.5 | 49.5 | 30.1 | 41.3 | 29 |
28 | 286 | 271 | 271 | 297 | 64.3 | 46.1 | 73.9 | 48.6 | 28.9 | 40.4 | 28 |
27 | 279 | 264 | 264 | 290 | 63.8 | 45.2 | 73.3 | 47.7 | 27.8 | 39.5 | 27 |
26 | 272 | 258 | 258 | 284 | 63.3 | 44.6 | 72.8 | 46.8 | 26.7 | 38.7 | 26 |
25 | 266 | 253 | 253 | 278 | 62.8 | 43.8 | 72.2 | 45.9 | 25.5 | 37.8 | 25 |
24 | 260 | 247 | 247 | 272 | 62.4 | 43.1 | 71.6 | 45.0 | 24.3 | 37.0 | 24 |
23 | 254 | 243 | 243 | 266 | 62.0 | 42.1 | 71.0 | 44.0 | 23.1 | 36.3 | 23 |
22 | 248 | 237 | 237 | 261 | 61.5 | 41.6 | 70.5 | 43.2 | 22.0 | 35.5 | 22 |
21 | 243 | 231 | 231 | 256 | 61.0 | 40.9 | 69.9 | 42.3 | 20.7 | 34.8 | 21 |
20 | 238 | 226 | 226 | 251 | 60.5 | 40.1 | 69.4 | 41.5 | 19.6 | 34.2 | 20 |
A In the table headings,
force refers to total test forces. |
Rockwell B Hardness Number, 100-kgf (HRB) |
Vickers Hardness Number (HV) |
Brinell Hardness Number, 3000-kgf, (HBS) |
Knoop Hardness Number, 500-gf, and Over (HK) |
Rockwell A Hardness Number, 60-kgf, (HRA) |
Rockwell F Hardness Number, 60-kgf, (HRF) |
Rockwell Superficial Hardness Number |
Rockwell B Hardness Number, 100-kgf, (HRB) |
||||
15-T Scale, 15-kgf, (HR 15-T) |
30-T Scale, 30-kgf, (HR 30-T) |
45-T Scale, 45-kgf, (HR 45-T) |
|||||||||
100 | 240 | 240 | 251 | 61.5 | --- | 93.1 | 83.1 | 72.9 | 100 | ||
99 | 234 | 234 | 246 | 60.9 | --- | 92.8 | 82.5 | 71.9 | 99 | ||
98 | 228 | 228 | 241 | 60.2 | --- | 92.5 | 81.8 | 70.9 | 98 | ||
97 | 222 | 222 | 236 | 59.5 | --- | 92.1 | 81.1 | 69.9 | 97 | ||
96 | 216 | 216 | 231 | 58.9 | --- | 91.8 | 80.4 | 68.9 | 96 | ||
95 | 210 | 210 | 226 | 58.3 | --- | 91.5 | 79.8 | 67.9 | 95 | ||
94 | 205 | 205 | 221 | 57.6 | --- | 91.2 | 79.1 | 66.9 | 94 | ||
93 | 200 | 200 | 216 | 57.0 | --- | 90.8 | 78.4 | 65.9 | 93 | ||
92 | 195 | 195 | 211 | 56.4 | --- | 90.5 | 77.8 | 64.8 | 92 | ||
91 | 190 | 190 | 206 | 55.8 | --- | 90.2 | 77.1 | 63.8 | 91 | ||
90 | 185 | 185 | 201 | 55.2 | --- | 89.9 | 76.4 | 62.8 | 90 | ||
89 | 180 | 180 | 196 | 54.6 | --- | 89.5 | 75.8 | 61.8 | 89 | ||
88 | 176 | 176 | 192 | 54.0 | --- | 89.2 | 75.1 | 60.8 | 88 | ||
87 | 172 | 172 | 188 | 53.4 | --- | 88.9 | 74.4 | 59.8 | 87 | ||
86 | 169 | 169 | 184 | 52.8 | --- | 88.6 | 73.8 | 58.8 | 86 | ||
85 | 165 | 165 | 180 | 52.3 | --- | 88.2 | 73.1 | 57.8 | 85 | ||
84 | 162 | 162 | 176 | 51.7 | --- | 87.9 | 72.4 | 56.8 | 84 | ||
83 | 159 | 159 | 173 | 51.1 | --- | 87.6 | 71.8 | 55.8 | 83 | ||
82 | 156 | 156 | 170 | 50.6 | --- | 87.3 | 71.1 | 54.8 | 82 | ||
81 | 153 | 153 | 167 | 50.0 | --- | 86.9 | 70.4 | 53.8 | 81 | ||
80 | 150 | 150 | 164 | 49.5 | --- | 86.6 | 69.7 | 52.8 | 80 | ||
79 | 147 | 147 | 161 | 48.9 | --- | 86.3 | 69.1 | 51.8 | 79 | ||
Rockwell B Hardness Number, 100-kgf (HRB) |
Vickers Hardness Number (HV) |
Brinell Hardness Number, 3000-kgf, (HBS) |
Knoop Hardness Number, 500-gf, and Over (HK) |
Rockwell A Hardness Number, 60-kgf, (HRA) |
Rockwell F Hardness Number, 60-kgf, (HRF) |
Rockwell Superficial Hardness Number |
Rockwell B Hardness Number, 100-kgf, (HRB) |
||||
15-T Scale, 15-kgf, (HR 15-T) |
30-T Scale, 30-kgf, (HR 30-T) |
45-T Scale, 45-kgf, (HR 45-T) |
|||||||||
78 | 144 | 144 | 158 | 48.4 | --- | 86.0 | 68.4 | 50.8 | 78 | ||
77 | 141 | 141 | 155 | 47.9 | --- | 85.6 | 67.7 | 49.8 | 77 | ||
76 | 139 | 139 | 152 | 47.3 | --- | 85.3 | 67.1 | 48.8 | 76 | ||
75 | 137 | 137 | 150 | 46.8 | 99.6 | 85.0 | 66.4 | 47.8 | 75 | ||
74 | 135 | 135 | 147 | 46.3 | 99.1 | 84.7 | 65.7 | 46.8 | 74 | ||
73 | 132 | 132 | 145 | 45.8 | 98.5 | 84.3 | 65.1 | 45.8 | 73 | ||
72 | 130 | 130 | 143 | 45.3 | 98.0 | 84.0 | 64.4 | 44.8 | 72 | ||
71 | 127 | 127 | 141 | 44.8 | 97.4 | 83.7 | 63.7 | 43.8 | 71 | ||
70 | 125 | 125 | 139 | 44.3 | 96.8 | 83.4 | 63.1 | 42.8 | 70 | ||
69 | 123 | 123 | 137 | 43.8 | 96.2 | 83.0 | 62.4 | 41.8 | 69 | ||
68 | 121 | 121 | 135 | 43.3 | 95.6 | 82.7 | 61.7 | 40.8 | 68 | ||
67 | 119 | 119 | 133 | 42.8 | 95.1 | 82.4 | 61.0 | 39.8 | 67 | ||
66 | 117 | 117 | 131 | 42.3 | 94.5 | 82.1 | 60.4 | 38.7 | 66 | ||
65 | 116 | 116 | 129 | 41.8 | 93.9 | 81.8 | 59.7 | 37.7 | 65 | ||
64 | 114 | 114 | 127 | 41.4 | 93.4 | 81.4 | 59.0 | 36.7 | 64 | ||
63 | 112 | 112 | 125 | 40.9 | 92.8 | 81.1 | 58.4 | 35.7 | 63 | ||
62 | 110 | 110 | 124 | 40.4 | 92.2 | 80.8 | 57.7 | 34.7 | 62 | ||
61 | 108 | 108 | 122 | 40.0 | 91.7 | 80.5 | 57.0 | 33.7 | 61 | ||
60 | 107 | 107 | 120 | 39.5 | 91.1 | 80.1 | 56.4 | 32.7 | 60 | ||
59 | 106 | 106 | 118 | 39.0 | 90.5 | 79.8 | 55.7 | 31.7 | 59 | ||
58 | 104 | 104 | 117 | 38.6 | 90.0 | 79.5 | 55.0 | 30.7 | 58 | ||
57 | 103 | 103 | 115 | 38.1 | 89.4 | 79.2 | 54.4 | 29.7 | 57 | ||
56 | 101 | 101 | 114 | 37.7 | 88.8 | 78.8 | 53.7 | 28.7 | 56 | ||
55 | 100 | 100 | 112 | 37.2 | 88.2 | 78.5 | 53.0 | 27.7 | 55 | ||
54 | --- | --- | 111 | 36.8 | 87.7 | 78.2 | 52.4 | 26.7 | 54 | ||
Rockwell B Hardness Number, 100-kgf (HRB) |
Vickers Hardness Number (HV) |
Brinell Hardness Number, 3000-kgf, (HBS) |
Knoop Hardness Number, 500-gf, and Over (HK) |
Rockwell A Hardness Number, 60-kgf, (HRA) |
Rockwell F Hardness Number, 60-kgf, (HRF) |
Rockwell Superficial Hardness Number |
Rockwell B Hardness Number, 100-kgf, (HRB) |
||||
15-T Scale, 15-kgf, (HR 15-T) |
30-T Scale, 30-kgf, (HR 30-T) |
45-T Scale, 45-kgf, (HR 45-T) |
|||||||||
53 | --- | --- | 110 | 36.3 | 87.1 | 77.9 | 51.7 | 25.7 | 53 | ||
52 | --- | --- | 109 | 35.9 | 86.5 | 77.5 | 51.0 | 24.7 | 52 | ||
51 | --- | --- | 108 | 35.5 | 86.0 | 77.2 | 50.3 | 23.7 | 51 | ||
50 | --- | --- | 107 | 35.0 | 85.4 | 76.9 | 49.7 | 22.7 | 50 | ||
49 | --- | --- | 106 | 34.6 | 84.8 | 76.6 | 49.0 | 21.7 | 49 | ||
48 | --- | --- | 105 | 34.1 | 84.3 | 76.2 | 48.3 | 20.7 | 48 | ||
47 | --- | --- | 104 | 33.7 | 83.7 | 75.9 | 47.7 | 19.7 | 47 | ||
46 | --- | --- | 103 | 33.3 | 83.1 | 75.6 | 47.0 | 18.7 | 46 | ||
45 | --- | --- | 102 | 32.9 | 82.6 | 75.3 | 46.3 | 17.7 | 45 | ||
44 | --- | --- | 101 | 32.4 | 82.0 | 74.9 | 45.7 | 16.7 | 44 | ||
43 | --- | --- | 100 | 32.0 | 81.4 | 74.6 | 45.0 | 15.7 | 43 | ||
42 | --- | --- | 99 | 31.6 | 80.8 | 74.3 | 44.3 | 14.7 | 42 | ||
41 | --- | --- | 98 | 31.2 | 80.3 | 74.0 | 43.7 | 13.6 | 41 | ||
40 | --- | --- | 97 | 30.7 | 79.7 | 73.6 | 43.0 | 12.6 | 40 | ||
39 | --- | --- | 96 | 30.3 | 79.1 | 73.3 | 42.3 | 11.6 | 39 | ||
38 | --- | --- | 95 | 29.9 | 78.6 | 73.0 | 41.6 | 10.6 | 38 | ||
37 | --- | --- | 94 | 29.5 | 78.0 | 72.7 | 41.0 | 9.6 | 37 | ||
36 | --- | --- | 93 | 29.1 | 77.4 | 72.3 | 40.3 | 8.6 | 36 | ||
35 | --- | --- | 92 | 28.7 | 76.9 | 72.0 | 39.6 | 7.6 | 35 | ||
34 | --- | --- | 91 | 28.2 | 76.3 | 71.7 | 39.0 | 6.6 | 34 | ||
33 | --- | --- | 90 | 27.8 | 75.7 | 71.4 | 38.3 | 5.6 | 33 | ||
32 | --- | --- | 89 | 27.4 | 75.2 | 71.0 | 37.6 | 4.6 | 32 | ||
31 | --- | --- | 88 | 27.0 | 74.6 | 70.7 | 37.0 | 3.6 | 31 | ||
30 | --- | --- | 87 | 26.6 | 74.0 | 70.4 | 36.3 | 2.6 | 30 | ||
A In table headings, kgf
refers to total test force. |
Approximate Hardness
Conversion Numbers for
|
Rockwell Hardness Number, B Scale (100-kgf, 1⁄16-in. (1.588-mm) ball) (HRB) |
Brinell Hardness Number (3000-kgf, 10-mm ball) (HBS) |
100 | 256 |
99 | 248 |
98 | 240 |
97 | 233 |
96 | 226 |
95 | 219 |
94 | 213 |
93 | 207 |
92 | 202 |
91 | 197 |
90 | 192 |
89 | 187 |
88 | 183 |
87 | 178 |
86 | 174 |
85 | 170 |
84 | 167 |
83 | 163 |
82 | 160 |
81 | 156 |
80 | 153 |
79 | 150 |
78 | 147 |
77 | 144 |
76 | 142 |
75 | 139 |
74 | 137 |
73 | 135 |
72 | 132 |
71 | 130 |
70 | 128 |
69 | 126 |
68 | 124 |
67 | 122 |
66 | 120 |
65 | 118 |
64 | 116 |
63 | 114 |
62 | 113 |
61 | 111 |
60 | 110 |
Rockwell Hardness Number | Rockwell Superficial Hardness Number | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
C Scale, 150-kgf Diamond Penetrator (HRC) |
A Scale, 60-kgf, Diamond Penetrator (HRA) |
15-N Scale, 15-kgf, Superficial Diamond Penetrator (HR 15-N) |
30-N Scale, 30-kgf, Superficial Diamond Penetrator (HR 30-N) |
45-N Scale, 45-kgf, Superficial Diamond Penetrator (HR 45-N) |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
48 | 74.4 | 84.1 | 66.2 | 52.1 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
47 | 73.9 | 83.6 | 65.3 | 50.9 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
46 | 73.4 | 83.1 | 64.5 | 49.8 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
45 | 72.9 | 82.6 | 63.6 | 48.7 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
44 | 72.4 | 82.1 | 62.7 | 47.5 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
43 | 71.9 | 81.6 | 61.8 | 46.4 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
42 | 71.4 | 81.0 | 61.0 | 45.2 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
41 | 70.9 | 80.5 | 60.1 | 44.1 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
40 | 70.4 | 80.0 | 59.2 | 43.0 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
39 | 69.9 | 79.5 | 58.4 | 41.8 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
38 | 69.3 | 79.0 | 57.5 | 40.7 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
37 | 68.8 | 78.5 | 56.6 | 39.6 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
36 | 68.3 | 78 | 55.7 | 38.4 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
35 | 67.8 | 77.5 | 54.9 | 37.3 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
34 | 67.3 | 77.0 | 54.0 | 36.1 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
33 | 66.8 | 76.5 | 53.1 | 35.0 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
32 | 66.3 | 75.9 | 52.3 | 33.9 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
31 | 65.8 | 75.4 | 51.4 | 32.7 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
30 | 65.3 | 74.9 | 50.5 | 31.6 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
29 | 64.8 | 74.4 | 49.6 | 30.4 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
28 | 64.3 | 73.9 | 48.8 | 29.3 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
27 | 63.8 | 73.4 | 47.9 | 28.2 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
26 | 63.3 | 72.9 | 47.0 | 27.0 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
25 | 62.8 | 72.4 | 46.2 | 25.9 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
24 | 62.3 | 71.9 | 45.3 | 24.8 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
23 | 61.8 | 71.3 | 44.4 | 23.6 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
22 | 61.3 | 70.8 | 43.5 | 22.5 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
21 | 60.8 | 70.3 | 42.7 | 21.3 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
20 | 60.3 | 69.8 | 41.8 | 20.2 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
|
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
A In table headings, kgf or gf refers to
total test force. |
ASTM A 370 Mechanical Testing of Steel Products | |
Conversion Tables for Hardness Scales-Cast Rolls | |
Hardness Scales Conversion Table - Forged Rolls | |
Steel Hardness Conversion Table |
[_borders/bottom.htm] |